Информация о статье:

Раздел/SectionЭлектроосаждение металлов и сплавовElectroplating of metals and alloys
Заглавие/Title

Электрохимический синтез сплава никель-рений и его электрокаталитические свойства

Electrochemical Synthesis of Nickel-Renium Alloy and Its Electrocatalytic Characteristics

Авторы/AuthorsКузнецов В.В., Гамбург Ю.Д., Жуликов В.В., Баталов Р.С., Филатова Е.А.Kuznetsov V.V., Gamburg Yu.D., Zhulikov V.V., Batalov R.S., Filatova E.A.
Страницы/Pages4-12
Ключевые слова
Keywords
electrolytic alloys, hydrogen evolution reaction, nickel, rhenium, molybdenum, электролитические сплавы, реакция выделения водорода, никель, рений, электрокатализ
Аннотация
Description
Исследованы химический и фазовый состав сплавов Ni-Re, полученных электроосаждением из цитратных электролитов, а также их каталитическая активность в реакции электрохимического выделения водорода (РВВ) в щелочных растворах. Проанализировано влияние химического состава сплава на кинетику РВВ. Высказано предположение, что высокая каталитическая активность электролитических осадков никель-рений связана с наличием в их составе оксидов рения.Ni-Re cathodes catalytic activity towards hydrogen evolution reaction (HER) in the solution of sodium hydroxide was studied. Ni-Re coatings were deposited onto the surface of a copper substrate from ammonium-citrate solutions in the galvanostatic regime. The obtained deposits were examined by modern physical methods, namely: XPS, XRD, and SEM with X-ray microanalyzer. It was established that the full reduction of nickel species occurs during electrodeposition, while rhenium species electroreduction is incomplete. Large amounts of Rh(IV) oxide were detected in the electrode deposits. The increase in rhenium content in Ni-Re deposits caused the increase in their catalytic activity towards HER that is accompanied by Tafel slope decreasing. This is due to high surface coverage by adsorbed hydrogen atoms (?H) and its dependence from electrode potential. The deposits obtained by electrodeposition contain a high amount of sorbed hydrogen. Ni-Re coatings immediately after electrodeposition were X-ray amorphous. Heat treatment at 450 °C in vacuum resulted in the change in their crystal structure. After heat treatment, they were the solid solution of nickel in hexagonal rhenium lattice. This resulted in the decrease in catalytic activity towards HER.
Ссылка на
Link for citation
Текст/Texthttp://elibrary.ru/item.asp?id=36552094

 